Generic Name: 乙烯四氟乙烯共聚物(ETFE) - 提供方: The ChemoursCompany
DuPont™ Tefzel ® fluoropolymer resins offer mechanical strengthand toughness along with resistance to heat and chemicals. Inaddition, they provide easy processing, high specific dielectricstrength, and a low coefficient of friction. For these reasons,Tefzel ® resins are widely used to make compact wire and cableconstructions that provide long, reliable service in demandingenvironments.
Tefzel ® 750 retains the traditional characteristics of Tefzel ®resins while providing some new property advantages, includingincreased flexibility and improved retention of properties afteraging at elevated temperatures, higher limiting oxygen index, andlong-term service life at higher temperatures than other Tefzel ®resins.
Underwriters Laboratories, Inc. (UL) has rated wire insulated withTefzel ® 750 (10 mil for 600V, 6 mil for 300V) for service inappliances at a maximum continuous operating temperature of 200°C(392°F). This rating was determined under the guidelines of ULSubject 758 for appliance wiring material. Upper servicetemperatures for other applications should be determined under theguidelines for those applications. Temperature ratings may not bethe same as the rating for appliance wire because the testprocedures are different.
Typical End Products
Tefzel ™ ETFE 750 fluoroplastic resin can be used for wire serviceat up to 200 °C (392 °F).Tefzel ™ ETFE 750 can also be used asinsulation for applications where customers need the basic benefitsof Tefzel ™ together with increased flexibility and improvedretention of properties after aging at elevated
temperatures. Flexibility is desirable for ease of handling duringmaintenance and repair procedures.
与典型值比较 - Upgrade tocompare! 与黄卡比较
单位: SI
总览
材料状态
已商用:当前有效
资料 1Technical Datasheet (English)
UL 黄卡 2E54681-244670
搜索 UL 黄卡The Chemours Company
Tefzel®
供货地区北美洲
拉丁美洲
欧洲
亚太地区
特性低摩擦系数
共聚物
良好的加工性能
良好的柔韧性
耐化学品性能,良好
耐热性,高
韧性良好
用途电线电缆应用
电子绝缘
形式粒子
加工方法挤出
物理性能额定值
单位制
测试方法
密度 / 比重1.75 到 1.79
g/cm³
ASTM D792熔流率(熔体流动速率) (297°C/5.0kg)7.0
g/10 min
ASTM D3159机械性能额定值
单位制
测试方法
抗张强度ASTM D170823°C
37.9
MPa
140°C
11.4
MPa
160°C
8.62
MPa
180°C
6.21
MPa
200°C
3.45
MPa
伸长率
ASTM D1708断裂,23°C
300
%
断裂, 140°C
600
%
断裂, 160°C
650
%
断裂, 180°C
600
%
断裂, 200°C
600
%
弯曲模量
645
MPa
ASTM D790热性能额定值
单位制
测试方法
熔融温度219 到 254
°C
ASTM D3159可燃性额定值
单位制
测试方法
极限氧指数34
%
ASTM D2863补充信息额定值
单位制
测试方法
MIT Flexural Life120000
挤出
额定值
单位制
料筒1区温度
288
°C
料筒2区温度
316
°C
料筒3区温度
321
°C
接头温度
321
°C
熔体温度
332 到 335
°C
口模温度
332
°C