Generic Name: 聚偏二氟乙烯(PVDF) - 提供方: SolvaySpecialty Polymers
Solef® 9009 PVDF homopolymer is a semi-crysalline fluoropolymer.Solef® film is chemically inert to most acids, aliphatic andaromatic organic compounds, chlorinated solvents and alcohols.
Solef® PVDF flim has a very high purity, abrasion resistancecomparable to that of polyamides and relatively low coefficient offriction. These films can be used in a wide range of temperaturesand have excellent intrinsic fire resistance.
Solef® PVDF films have demonstrated excellent weathering propertiesand are extremely resistant to UV radiation and common industrialand environmental pollutants.
Solef® PVDF films can be used in a wide range of applications,including release films, filters, chemical resistance lining,outdoor UV resistant needs as well as electric and electronicapplications.
与典型值比较 - Upgrade tocompare!
单位: SI
总览
材料状态
已商用：当前有效
资料 1Technical Datasheet
搜索 UL 黄卡Solvay Specialty Polymers
供货地区北美洲
拉丁美洲
欧洲
亚太地区
特性均聚物
外观半透明
物理性能额定值
单位制
测试方法
密度 / 比重1.75 到 1.80
g/cm³
ASTM D792吸水率 (24 hr,23°C)< 0.040
%
ASTM D570机械性能额定值
单位制
测试方法
摩擦系数ASTM D1894与自身 -动态
0.15 到 0.35
与自身 - 静态
0.20 到 0.40
泰伯耐磨性 (1000 Cycles, 1000 g, CS-10 转轮)
5.00 到 10.0
mg
ASTM D4060撕裂阻力- MD8.9
cN
ASTM D1004薄膜额定值
单位制
测试方法
薄膜厚度 - 经测试--
25
µm
-- 3
50
µm
-- 4
130
µm
割线模量
ASTM D882MD
2000
MPa
TD
2100
MPa
抗张强度
ASTM D882MD :屈服
55.0
MPa
TD : 屈服
56.0
MPa
MD : 断裂
57.0
MPa
TD : 断裂
54.0
MPa
伸长率
ASTM D882MD :屈服
6.0
%
TD : 屈服
6.2
%
MD : 断裂
200
%
TD : 断裂
250
%
落锤冲击
< 360
g
ASTM D1709B自由收缩 (130°C)0.70
%
ASTM D2732抗撕裂蔓延性 - MD350
gf
ASTM D1922面积系数108
ft²/lb/mil
热性能
额定值
单位制
测试方法
玻璃转化温度-40.0
°C
ASTM D4065熔融温度162 到 168
°C
ASTM D3418结晶峰温度 (DSC)133 到 140
°C
ASTM D3418线形热膨胀系数 - 流动1.4E-4
cm/cm/°C
ASTM D696比热 (100°C)1600
J/kg/°C
ASTM C351导热系数0.20
W/m/K
ASTM C177电气性能额定值
单位制
测试方法
表面电阻率> 1.0E+14
ohms
ASTM D257体积电阻率> 1.0E+14
ohms·cm
ASTM D257介电强度 (23°C, 1.00mm)20 到 25
kV/mm
ASTM D149介电常数7.50
ASTM D150可燃性
额定值
单位制
测试方法
极限氧指数 (3.00 mm)44
%
ASTM D2863